丙烯酸环氧酯底漆
composition: acrylic modification epoxy resin, anti rust pigments of iron oxide red, iron oxide yellow and zinc yellow, extender pigment, additive, organic solvent.
characteristic: the film is hard and adhesive and can dry fast. it enjoys the same three proof performance of h06 2primer, the character of moisture resistance, acid resistance and anti resistance will be enhanced when using with phosphating primer. the paints of iron red and iron buff are suitable for the ferrous metal. the paint of zinc yellow is suitable for light metal.
projects standards:
|
projects |
standards |
|
colour and appearance of the film |
iron red, iron oxide black, zinc yellow |
|
viscosity(paint 4cup),s no less than |
50 |
|
fineness µm no more than |
iron red, iron oxide black 60,zinc yellow 50 |
|
drying time, 25±1℃ no more than
drying time surface min
hard drying time
baking（120±2℃）min no more than |
20
12
20 |
|
hardness no less than |
0.40 |
|
flexibility, cm |
1 |
|
impact strength, kg＆#8226;cm |
50 |
|
adhesion, level, no more than |
1 |
|
salt water resistance（96h） |
no foaming, no rust |
|
nitro resistance |
no foaming, no bleeding, no expansion |
constrution reference:
1. remove the rust and the grease then brush a layer of phosphating paint before using it.
2. stir the paint before work.use the special diluent. spraying and brush painting are both available.
3. when the paint hard dries the putty and topcoat can be used.
4. this paint can be used with the advanced auto paint, alkyd paint, perchloroethylene and acrylic topcoat. |